| Type |
Model number |
Properties |
Characteristics |
Dosage |
| 1，Dispersing agents |
| Titanium white powder and inorganic pigments |
NEO-1503 |
Acidic polymer
|
High dispersion whiteness as used for titanium white powder;
obvious viscosity deduction, excellent leveling performance and high brilliancy.
|
1-4%（for pigments） |
| NEO-1510 |
Middle molecular polyurethane |
high performance of dispersion and viscosity reduction, obvious settlement prevention and resistance of floating color and blur. |
1-4%（for pigments） |
| Organic pigments and carbon black |
NEO-1201 |
Macro molecule polyurethane
|
Obvious viscosity reduction and stabilization effects for hard scattered pigments.
|
20-150%（for pigments） |
| NEO-1202 |
Macro molecule polyurethane
|
High cost performance and stability.
|
20-150%（for pigments） |
| NEO-1222 |
Polyurethane with special structure |
Wide versatility for various systems;
excellent viscosity reduction, stabilization and color phase for carbon black. |
20-150%（for pigments） |
| Economic type dispersing agents |
NEO-1604 |
Amphoteric wetting dispersing agents
|
Versatility and good pigment wetting property.
|
0.5-10%（for pigments） |
| NEO-1607 |
Wetting dispersing agents
|
exclusive use for alcohol aid systems, with high cost performance.
|
0.5-10%（for pigments） |
| NEO-1730 |
Exclusive dispersing agents for carbon black |
Special dispersing agents used for primary carbon black, such as C311;
Excellent viscosity reduction, good carbon black color phase and high stability. |
10-40%（for carbon black） |
| Co-grinding |
NEO-1665 |
Acid wetting agent containing silicon
|
notable effect for preventing floating color and blur for co-grinding, and valid as added later.
|
0.1-0.5%（for formula） |
| NEO-1666 |
Acid wetting agent
|
Good co-grinding effects for preventing floating color and blur, and high cost performance.
|
0.1-0.5%（for formula） |
| NEO-1667 |
Acid wetting agent containing silicon |
Excellent color expanding, floating color and blur preventing performances. |
0.1-0.5%（for formula） |
| 2，Leveling agents |
| Polyacrylic ester |
NEO-3054 |
Polyacrylic ester |
Excellent long wave leveling and defoaming effects.
|
0.2-0.8%（for formula） |
| NEO-3055 |
Polyacrylic ester |
High leveling speed and good foam breaking effects.
|
0.2-0.8%（for formula） |
| NEO-3058 |
Polyacrylic ester |
Excellent leveling and compatibility performance. |
0.3-1.0%（for formula） |
| Fluorine modified Polyacrylic ester |
NEO-3166 |
Fluorine carbon |
Excellent shrink cavity resistance, high leveling speed and favorable aluminum powder orientation.
|
0.1-0.5%（for formula） |
| NEO-3170 |
Fluorine modified Polyacrylic ester |
Excellent long wave leveling effect and defoaming capability.
|
0.2-0.8%（for formula） |
| NEO-3172 |
Fluorine modified Polyacrylic ester |
Excellent compatibility, leveling performance and appliance for middle and high polarities.
|
0.3-1.0%（for formula） |
| NEO-3177 |
Fluorine modified Polyacrylic ester |
Excellent wetting property of base material, leveling performance and appliance for middle and high polarities. |
0.3-1.0%（for formula） |
| Organic silicon |
NEO-3006 |
Polyether modified organic silicon |
excellent leveling performance, shrink cavity and oil fouling resistance, and applicability for plastic paint.
|
0.2-1.0%（for formula） |
| NEO-3606 |
Aralkyl modified organic silicon
|
High performances for aluminum powder and pearl powder orientation, and excellent defoaming performance.
|
0.05-0.2%（for formula） |
| NEO-3633 |
Polyether modified organic silicon |
Excellent leveling performance, compatibility and high smoothness.
|
0.1-0.3%（for formula） |
| NEO-3645 |
Polyether modified organic silicon |
Excellent leveling performance and hand feeling. |
0.1-0.3%（for formula） |
| 3，Defoaming agents |
| Organic silicon |
NEO-5201 |
Modified organic silicon |
Balanced defoaming performance and compatibility; high safety. |
0.2-0.8%（for formula） |
| Fluorine silicon |
NEO-5606 |
Fluorine silicon superpolymer |
Favorable defoaming capability, especially bubble breaking capability.
|
0.1-0.5%（for formula） |
| NEO-5606D |
Fluorine silicon superpolymer |
Low odor type of NEO-5606D, with high defoaming capability. |
0.1-0.5%（for formula） |
| 4，Special blending agents |
| Acid catalyst |
NEO-8925 |
Closed dodecylbenzene sulfonic acid
|
High catalysis efficiency for stoving varnish systems, high compatibility and brilliancy.
|
0.1-1.0%（for formula） |
| NEO-8945 |
Closed para-toluenesulfonic acid |
High catalysis efficiency for stoving varnish systems, with the minimum unsealing temperature of 80℃. |
0.1-1.0%（for formula） |
| Adhesive force accelerant |
NEO-8980 |
Epoxy phosphoric acid ester |
High compatibility and obvious adhesive force improvement for metal base material;
Fairly good effects of acid catalysis solidification for stoving varnish systems.
|
0.5-2.0%（for formula） |
| NEO-8982 |
Epoxy phosphoric acid ester |
High performance for improving adhesive force of metal base material;
notable improvement of abrasion resistance for baking pre-coating. |
1-5%（for formula） |